5mm 10mm Thickness Aluminium Sheet Plate 1050 1060 1100 Alloy
Aluminum sheets are used in a variety of industries for their many properties. Some of these properties include:
- Lightweight: Aluminum is about one third the weight of steel, making it ideal for use in applications where weight is a factor.
- Corrosion resistant: Aluminum naturally forms a protective oxide coating when exposed to air, making it resistant to corrosion.
- Non-magnetic: Aluminum is not attracted to magnets, making it ideal for use in applications where magnetic fields are present.
- Ductile: Aluminum can be easily drawn into wire or formed into sheets without breaking.
- Malleable: Aluminum can be hammered or rolled into thin sheets without breaking.
- Non-toxic: Aluminum is safe to use in food and beverage containers as it does not leach into the contents.
Specification
| GB/T 3190 | ISO 2092 | ASTM B221 | JIS H4040 |
| 1060 | Al99.6 | 1060 | 1070 |
| 1100 | Al99.0Cu | 1100 | 1100 |
| 2024 | AlCu4Mg1 | 2024 | 2024 |
| 3003 | AlMn1Cu | 3003 | 3003 |
| 5052 | AlMg2.5 | 5052 | 5052 |
| 5083 | AlMg4.5-Mn0.7 | 5083 | 5083 |
| 6061 | AlMg1SiCu | 6061 | 6061 |
| 7075 | AlZn5.5-CuMg | 7075 | 7075 |
| GB/T 3190 | Chemical Composition(%) | ||||||||
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al | |
| 1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.05 | 0.03 | 99.6 |
| 1100 | 0.95 Si+Fe | | 0.05-0.20 | 0.05 | - | - | 0.1 | - | 99 |
| 2024 | 0.5 | 0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | 0.1 | 0.25 | 0.15 | Balance |
| 3003 | 0.6 | 0.7 | 0.05-0.20 | 1.0-1.5 | - | - | 0.1 | - | Balance |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | 0.1 | - | Balance |
| 5083 | 0.4 | 0.4 | 0.1 | 0.40-1.0 | 4.0-4.9 | 0.05-0.25 | 0.25 | 0.15 | Balance |
| 6061 | 0.40-0.8 | 0.7 | 0.15-0.40 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | Balance |
| 7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | 5.1-6.1 | 0.2 | Balance |
| Mechanical Property | ||||||||
| ALUMINUM ALLOY | Grade | Normal Temper | Temper | Tensile Strength N/mm² | Yield Strength N/mm² | Elongation% | Brinell Hardness HB | |
| Plate | Bar | |||||||
| 1XXX | 1050 | O,H112,H | O | 78 | 34 | 40 | - | 20 |
| 1060 | O,H112,H | O | 70 | 30 | 43 | - | 19 | |
| Al-Cu (2XXX) | 2019 | O,T3,T4,T6,T8 | T851 | 450 | 350 | 10 | - | - |
| 2024 | O,T4 | T4 | 470 | 325 | 20 | 17 | 120 | |
| Al-Mn (3XXX) | 3003 | | O | 110 | 40 | 30 | 37 | 28 |
| 3004 | O,H112,H | O | 180 | 70 | 20 | 22 | 45 | |
| Al-Si (4XXX) | 4032 | O,T6,T62 | T6 | 380 | 315 | - | 9 | 120 |
| Al-Mg (5XXX) | 5052 | O,H112,H | H34 | 260 | 215 | 10 | 12 | 68 |
| 5083 | O,H112,H | O | 290 | 145 | - | 20 | - | |
| Al-Mg-Si (6XXX) | 6061 | O,T4,T6,T8 | T6 | 310 | 275 | 12 | 15 | 95 |
| 6063 | O,T1,T5,T6,T8 | T5 | 185 | 145 | 12 | - | 60 | |
| Al-Zn-Mg (7XXX) | 7003 | T5 | T5 | 315 | 255 | 15 | - | 85 |
| 7075 | O,T6 | T6 | 570 | 505 | 11 | 9 | 150 | |